Title: Nanosized Precipitates In H13 Tool Steel Low Temperature Plasma Nitriding
Author: Zagonel L.F.
Bettini J.
Basso R.L.O.
Paredez P.
Pinto H.
Lepienski C.M.
Alvarez F.
Abstract: A comprehensive study of pulsed nitriding in AISI H13 tool steel at low temperature (400°C) is reported for several durations. X-ray diffraction results reveal that a nitrogen enriched compound (ε-Fe 2-3N, iron nitride) builds up on the surface within the first process hour despite the low process temperature. Beneath the surface, X-ray Wavelength Dispersive Spectroscopy (WDS) in a Scanning Electron Microscope (SEM) indicates relatively higher nitrogen concentrations (up to 12at.%) within the diffusion layer while microscopic nitrides are not formed and existing carbides are not dissolved. Moreover, in the diffusion layer, nitrogen is found to be dispersed in the matrix and forming nanosized precipitates. The small coherent precipitates are observed by High-Resolution Transmission Electron Microscopy (HR-TEM) while the presence of nitrogen is confirmed by electron energy loss spectroscopy (EELS). Hardness tests show that the material hardness increases linearly with the nitrogen concentration, reaching up to 14.5GPa in the surface while the Young Modulus remains essentially unaffected. Indeed, the original steel microstructure is well preserved even in the nitrogen diffusion layer. Nitrogen profiles show a case depth of about ~43μm after nine hours of nitriding process. These results indicate that pulsed plasma nitriding is highly efficient even at such low temperatures and that at this process temperature it is possible to form thick and hard nitrided layers with satisfactory mechanical properties. This process can be particularly interesting to enhance the surface hardness of tool steels without exposing the workpiece to high temperatures and altering its bulk microstructure. © 2012 Elsevier B.V.
Citation: Surface And Coatings Technology. , v. 207, n. , p. 72 - 78, 2012.
Rights: fechado
Identifier DOI: 10.1016/j.surfcoat.2012.05.081
Date Issue: 2012
Appears in Collections:Unicamp - Artigos e Outros Documentos

Files in This Item:
There are no files associated with this item.

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.